NOTES:
1.MATERIAL SPECIFICATION
1-1.HOUSING: LCP+30% G.F BLACK UL94 V-0.
1-2.CONTACT: BRASS(C2680).
1-3.SHELL:BRASS(C2680).
2.PLATING SPECIFICATION
2-1.CONTACT: NI50u'' UNDER PLATED,GOLD FLASH PLATED ON THE FUNCTIONAL
AREA OF CONTACT,GOLD PLATING OR TIN ON SOLDER AREA.
2-2.SHELL: NICKEL PLATED.
3.MECHANICAL PERFORMANCE
3-1.INSERTION FORCE: 44.1N (4.5 KGF) MAX.
3-2.WITHDRAWAL FORCE: 4.9N~39.2N(0.5KGF~4.0KGF).
3-3.DURABILITY: 5000 CYCLES.
4.ELECTRICAL PERFORMANCE
4-1.CURRENT RATING: 0.5A.
4-2.LLCR: CONTACT: 30 m? MAX(INITIAL), SHELL: 50 m? MAX(INITIAL).
4-3.INSULATION RESISTANCE:
A:UNMATED: 100 M? MIN. AT 500V DC.
B:MATED: 10 M? MIN. AT 150V DC.
4-4.DIELECTRIC WITHSTAND VOLTAGE: 300V AC/60S(MATED), 500V AC/60S(UNMATED).
5.IR REFLOW: THE PEAK TEMPERATURE ON BOARD SHALL BE MAINTAINED FOR 10 SECONDS AT 260±5°C.
6.OPERATING TEMPERATURE RANGE: -25°C~85°C(WITHOUT LOSS FUNCTION).